EN 1.3553 Steel vs. 2219 Aluminum
EN 1.3553 steel belongs to the iron alloys classification, while 2219 aluminum belongs to the aluminum alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.3553 steel and the bottom bar is 2219 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 72 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 720 | |
| 180 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 540 | |
| 230 |
| Melting Completion (Liquidus), °C | 1620 | |
| 640 |
| Melting Onset (Solidus), °C | 1570 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 870 |
| Thermal Conductivity, W/m-K | 24 | |
| 110 to 170 |
| Thermal Expansion, µm/m-K | 12 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 28 to 44 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 81 to 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 11 |
| Density, g/cm3 | 8.4 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 8.2 |
| Embodied Energy, MJ/kg | 130 | |
| 150 |
| Embodied Water, L/kg | 96 | |
| 1130 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 44 |
| Strength to Weight: Axial, points | 24 | |
| 16 to 43 |
| Strength to Weight: Bending, points | 21 | |
| 23 to 44 |
| Thermal Diffusivity, mm2/s | 6.4 | |
| 42 to 63 |
| Thermal Shock Resistance, points | 21 | |
| 8.2 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 91.5 to 93.8 |
| Carbon (C), % | 0.78 to 0.86 | |
| 0 |
| Chromium (Cr), % | 3.9 to 4.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 5.8 to 6.8 |
| Iron (Fe), % | 80.7 to 83.7 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 0.4 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 4.7 to 5.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.020 to 0.1 |
| Tungsten (W), % | 6.0 to 6.7 | |
| 0 |
| Vanadium (V), % | 1.7 to 2.0 | |
| 0.050 to 0.15 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 0 | |
| 0.1 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |