EN 1.3558 Steel vs. AWS E308Mo
Both EN 1.3558 steel and AWS E308Mo are iron alloys. They have 70% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.3558 steel and the bottom bar is AWS E308Mo.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 290 |
| Melting Completion (Liquidus), °C | 1810 | |
| 1440 |
| Melting Onset (Solidus), °C | 1760 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 470 |
| Thermal Conductivity, W/m-K | 20 | |
| 16 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 2.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 19 |
| Density, g/cm3 | 9.3 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 3.8 |
| Embodied Energy, MJ/kg | 130 | |
| 53 |
| Embodied Water, L/kg | 90 | |
| 160 |
Common Calculations
| PREN (Pitting Resistance) | 35 | |
| 28 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 23 | |
| 22 |
| Strength to Weight: Bending, points | 20 | |
| 20 |
| Thermal Diffusivity, mm2/s | 5.3 | |
| 4.2 |
| Thermal Shock Resistance, points | 22 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0.7 to 0.8 | |
| 0 to 0.080 |
| Chromium (Cr), % | 3.9 to 4.3 | |
| 18 to 21 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.75 |
| Iron (Fe), % | 73.7 to 77.6 | |
| 59.6 to 70.5 |
| Manganese (Mn), % | 0 to 0.4 | |
| 0.5 to 2.5 |
| Molybdenum (Mo), % | 0 to 0.6 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 0 | |
| 9.0 to 12 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Tungsten (W), % | 17.5 to 19 | |
| 0 |
| Vanadium (V), % | 1.0 to 1.3 | |
| 0 |