EN 1.3963 Alloy vs. C19100 Copper
EN 1.3963 alloy belongs to the iron alloys classification, while C19100 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.3963 alloy and the bottom bar is C19100 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 29 | |
| 17 to 37 |
| Poisson's Ratio | 0.3 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 43 |
| Shear Strength, MPa | 290 | |
| 170 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 440 | |
| 250 to 630 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 75 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 210 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1080 |
| Melting Onset (Solidus), °C | 1390 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 390 |
| Thermal Expansion, µm/m-K | 1.6 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 33 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 4.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 66 | |
| 43 |
| Embodied Water, L/kg | 110 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 60 to 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 24 to 1310 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 15 | |
| 7.7 to 20 |
| Strength to Weight: Bending, points | 16 | |
| 9.9 to 18 |
| Thermal Shock Resistance, points | 110 | |
| 8.9 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0 |
| Copper (Cu), % | 0 | |
| 96.5 to 98.6 |
| Iron (Fe), % | 60.5 to 64.9 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 35 to 37 | |
| 0.9 to 1.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0.15 to 0.35 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0.1 to 0.2 | |
| 0 |
| Tellurium (Te), % | 0 | |
| 0.35 to 0.6 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |