EN 1.3975 Stainless Steel vs. ASTM A369 Grade FP92
Both EN 1.3975 stainless steel and ASTM A369 grade FP92 are iron alloys. They have 72% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.3975 stainless steel and the bottom bar is ASTM A369 grade FP92.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 27 | |
| 19 |
| Fatigue Strength, MPa | 230 | |
| 330 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 320 | |
| 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 590 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1490 |
| Melting Onset (Solidus), °C | 1320 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 470 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 11 |
| Density, g/cm3 | 7.5 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 2.8 |
| Embodied Energy, MJ/kg | 47 | |
| 40 |
| Embodied Water, L/kg | 150 | |
| 89 |
Common Calculations
| PREN (Pitting Resistance) | 21 | |
| 14 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 | |
| 620 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 26 | |
| 24 |
| Strength to Weight: Axial, points | 24 | |
| 25 |
| Strength to Weight: Bending, points | 22 | |
| 22 |
| Thermal Shock Resistance, points | 15 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0.0010 to 0.0060 |
| Carbon (C), % | 0 to 0.050 | |
| 0.070 to 0.13 |
| Chromium (Cr), % | 16 to 18 | |
| 8.5 to 9.5 |
| Iron (Fe), % | 58.2 to 65.4 | |
| 85.8 to 89.1 |
| Manganese (Mn), % | 7.0 to 9.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 8.0 to 9.0 | |
| 0 to 0.4 |
| Niobium (Nb), % | 0 | |
| 0.040 to 0.090 |
| Nitrogen (N), % | 0.080 to 0.18 | |
| 0.030 to 0.070 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.020 |
| Silicon (Si), % | 3.5 to 4.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 1.5 to 2.0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.010 |