EN 1.3975 Stainless Steel vs. EN 1.6582 Steel
Both EN 1.3975 stainless steel and EN 1.6582 steel are iron alloys. They have 66% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.3975 stainless steel and the bottom bar is EN 1.6582 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 190 to 300 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 620 to 1750 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 440 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1460 |
| Melting Onset (Solidus), °C | 1320 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 470 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 3.6 |
| Density, g/cm3 | 7.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 1.7 |
| Embodied Energy, MJ/kg | 47 | |
| 22 |
| Embodied Water, L/kg | 150 | |
| 56 |
Common Calculations
| PREN (Pitting Resistance) | 21 | |
| 2.2 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 26 | |
| 24 |
| Strength to Weight: Axial, points | 24 | |
| 22 to 62 |
| Strength to Weight: Bending, points | 22 | |
| 21 to 41 |
| Thermal Shock Resistance, points | 15 | |
| 18 to 51 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.3 to 0.38 |
| Chromium (Cr), % | 16 to 18 | |
| 1.3 to 1.7 |
| Iron (Fe), % | 58.2 to 65.4 | |
| 94.7 to 96.5 |
| Manganese (Mn), % | 7.0 to 9.0 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0.15 to 0.3 |
| Nickel (Ni), % | 8.0 to 9.0 | |
| 1.3 to 1.7 |
| Nitrogen (N), % | 0.080 to 0.18 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.035 |
| Silicon (Si), % | 3.5 to 4.5 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.035 |