EN 1.4000 Stainless Steel vs. Z40101 Zinc

EN 1.4000 stainless steel belongs to the iron alloys classification, while Z40101 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4000 stainless steel and the bottom bar is Z40101 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 22
44
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 76
35
Tensile Strength: Ultimate (UTS), MPa 500
130
Tensile Strength: Yield (Proof), MPa 260
110

Thermal Properties

Latent Heat of Fusion, J/g 280
110
Maximum Temperature: Mechanical, °C 760
90
Melting Completion (Liquidus), °C 1440
410
Melting Onset (Solidus), °C 1400
400
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 30
110
Thermal Expansion, µm/m-K 11
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
27
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
37

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
11
Density, g/cm3 7.7
6.6
Embodied Carbon, kg CO2/kg material 1.9
2.8
Embodied Energy, MJ/kg 27
53
Embodied Water, L/kg 100
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
56
Resilience: Unit (Modulus of Resilience), kJ/m3 180
69
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 18
5.7
Strength to Weight: Bending, points 18
8.9
Thermal Diffusivity, mm2/s 8.1
44
Thermal Shock Resistance, points 18
4.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 12 to 14
0
Copper (Cu), % 0
0.080 to 0.4
Iron (Fe), % 83.9 to 88
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0 to 0.020
Zinc (Zn), % 0
99.542 to 99.92