EN 1.4062 Stainless Steel vs. CR021A Copper

EN 1.4062 stainless steel belongs to the iron alloys classification, while CR021A copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is CR021A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 23 to 34
15
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 79
43
Tensile Strength: Ultimate (UTS), MPa 770 to 800
230
Tensile Strength: Yield (Proof), MPa 530 to 600
140

Thermal Properties

Latent Heat of Fusion, J/g 290
210
Maximum Temperature: Mechanical, °C 1030
200
Melting Completion (Liquidus), °C 1430
1090
Melting Onset (Solidus), °C 1380
1040
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 15
380
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
98
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
99

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 7.7
9.0
Embodied Carbon, kg CO2/kg material 2.6
2.6
Embodied Energy, MJ/kg 37
41
Embodied Water, L/kg 150
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170 to 230
31
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 910
83
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 28 to 29
7.1
Strength to Weight: Bending, points 24 to 25
9.3
Thermal Diffusivity, mm2/s 4.0
110
Thermal Shock Resistance, points 21 to 22
8.1

Alloy Composition

Bismuth (Bi), % 0
0 to 0.00050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 21.5 to 24
0
Copper (Cu), % 0
99.95 to 99.998
Iron (Fe), % 69.3 to 77.3
0
Lead (Pb), % 0
0 to 0.0050
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.45
0
Nickel (Ni), % 1.0 to 2.9
0
Nitrogen (N), % 0.16 to 0.28
0
Phosphorus (P), % 0 to 0.040
0.0020 to 0.0070
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.015
Sulfur (S), % 0 to 0.010
0