EN 1.4062 Stainless Steel vs. C67500 Bronze

EN 1.4062 stainless steel belongs to the iron alloys classification, while C67500 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is C67500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 23 to 34
14 to 33
Poisson's Ratio 0.27
0.3
Shear Modulus, GPa 79
40
Shear Strength, MPa 510
270 to 350
Tensile Strength: Ultimate (UTS), MPa 770 to 800
430 to 580
Tensile Strength: Yield (Proof), MPa 530 to 600
170 to 370

Thermal Properties

Latent Heat of Fusion, J/g 290
170
Maximum Temperature: Mechanical, °C 1030
120
Melting Completion (Liquidus), °C 1430
890
Melting Onset (Solidus), °C 1380
870
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 15
110
Thermal Expansion, µm/m-K 13
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
24
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
27

Otherwise Unclassified Properties

Base Metal Price, % relative 12
23
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 2.6
2.8
Embodied Energy, MJ/kg 37
47
Embodied Water, L/kg 150
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170 to 230
61 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 910
130 to 650
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 28 to 29
15 to 20
Strength to Weight: Bending, points 24 to 25
16 to 19
Thermal Diffusivity, mm2/s 4.0
34
Thermal Shock Resistance, points 21 to 22
14 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.25
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 21.5 to 24
0
Copper (Cu), % 0
57 to 60
Iron (Fe), % 69.3 to 77.3
0.8 to 2.0
Lead (Pb), % 0
0 to 0.2
Manganese (Mn), % 0 to 2.0
0.050 to 0.5
Molybdenum (Mo), % 0 to 0.45
0
Nickel (Ni), % 1.0 to 2.9
0
Nitrogen (N), % 0.16 to 0.28
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0.5 to 1.5
Zinc (Zn), % 0
35.1 to 41.7
Residuals, % 0
0 to 0.5