EN 1.4062 Stainless Steel vs. C72800 Copper-nickel

EN 1.4062 stainless steel belongs to the iron alloys classification, while C72800 copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is C72800 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 23 to 34
3.9 to 23
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 79
44
Shear Strength, MPa 510
330 to 740
Tensile Strength: Ultimate (UTS), MPa 770 to 800
520 to 1270
Tensile Strength: Yield (Proof), MPa 530 to 600
250 to 1210

Thermal Properties

Latent Heat of Fusion, J/g 290
210
Maximum Temperature: Mechanical, °C 1030
200
Melting Completion (Liquidus), °C 1430
1080
Melting Onset (Solidus), °C 1380
920
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 15
55
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
11
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
11

Otherwise Unclassified Properties

Base Metal Price, % relative 12
38
Density, g/cm3 7.7
8.8
Embodied Carbon, kg CO2/kg material 2.6
4.4
Embodied Energy, MJ/kg 37
68
Embodied Water, L/kg 150
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170 to 230
37 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 910
260 to 5650
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 28 to 29
17 to 40
Strength to Weight: Bending, points 24 to 25
16 to 30
Thermal Diffusivity, mm2/s 4.0
17
Thermal Shock Resistance, points 21 to 22
19 to 45

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.1
Antimony (Sb), % 0
0 to 0.020
Bismuth (Bi), % 0
0 to 0.0010
Boron (B), % 0
0 to 0.0010
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 21.5 to 24
0
Copper (Cu), % 0
78.3 to 82.8
Iron (Fe), % 69.3 to 77.3
0 to 0.5
Lead (Pb), % 0
0 to 0.0050
Magnesium (Mg), % 0
0.0050 to 0.15
Manganese (Mn), % 0 to 2.0
0.050 to 0.3
Molybdenum (Mo), % 0 to 0.45
0
Nickel (Ni), % 1.0 to 2.9
9.5 to 10.5
Niobium (Nb), % 0
0.1 to 0.3
Nitrogen (N), % 0.16 to 0.28
0
Phosphorus (P), % 0 to 0.040
0 to 0.0050
Silicon (Si), % 0 to 1.0
0 to 0.050
Sulfur (S), % 0 to 0.010
0 to 0.0025
Tin (Sn), % 0
7.5 to 8.5
Titanium (Ti), % 0
0 to 0.010
Zinc (Zn), % 0
0 to 1.0
Residuals, % 0
0 to 0.3