EN 1.4062 Stainless Steel vs. C74500 Nickel Silver

EN 1.4062 stainless steel belongs to the iron alloys classification, while C74500 nickel silver belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is C74500 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 23 to 34
3.0 to 24
Poisson's Ratio 0.27
0.32
Shear Modulus, GPa 79
44
Shear Strength, MPa 510
310 to 380
Tensile Strength: Ultimate (UTS), MPa 770 to 800
390 to 700
Tensile Strength: Yield (Proof), MPa 530 to 600
380 to 600

Thermal Properties

Latent Heat of Fusion, J/g 290
190
Maximum Temperature: Mechanical, °C 1030
170
Melting Completion (Liquidus), °C 1430
1020
Melting Onset (Solidus), °C 1380
970
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 15
45
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
9.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
29
Density, g/cm3 7.7
8.3
Embodied Carbon, kg CO2/kg material 2.6
3.4
Embodied Energy, MJ/kg 37
54
Embodied Water, L/kg 150
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170 to 230
12 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 910
620 to 1540
Stiffness to Weight: Axial, points 14
7.7
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 28 to 29
13 to 23
Strength to Weight: Bending, points 24 to 25
14 to 21
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 21 to 22
13 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 21.5 to 24
0
Copper (Cu), % 0
63.5 to 66.5
Iron (Fe), % 69.3 to 77.3
0 to 0.25
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 0 to 0.45
0
Nickel (Ni), % 1.0 to 2.9
9.0 to 11
Nitrogen (N), % 0.16 to 0.28
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.010
0
Zinc (Zn), % 0
21.2 to 27.5
Residuals, % 0
0 to 0.5