EN 1.4062 Stainless Steel vs. C82500 Copper

EN 1.4062 stainless steel belongs to the iron alloys classification, while C82500 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4062 stainless steel and the bottom bar is C82500 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 23 to 34
1.0 to 20
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 79
45
Tensile Strength: Ultimate (UTS), MPa 770 to 800
550 to 1100
Tensile Strength: Yield (Proof), MPa 530 to 600
310 to 980

Thermal Properties

Latent Heat of Fusion, J/g 290
240
Maximum Temperature: Mechanical, °C 1030
280
Melting Completion (Liquidus), °C 1430
980
Melting Onset (Solidus), °C 1380
860
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 15
130
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
20
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
21

Otherwise Unclassified Properties

Density, g/cm3 7.7
8.8
Embodied Carbon, kg CO2/kg material 2.6
10
Embodied Energy, MJ/kg 37
160
Embodied Water, L/kg 150
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170 to 230
11 to 94
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 910
400 to 4000
Stiffness to Weight: Axial, points 14
7.7
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 28 to 29
18 to 35
Strength to Weight: Bending, points 24 to 25
17 to 27
Thermal Diffusivity, mm2/s 4.0
38
Thermal Shock Resistance, points 21 to 22
19 to 38

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.15
Beryllium (Be), % 0
1.9 to 2.3
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 21.5 to 24
0 to 0.1
Cobalt (Co), % 0
0.15 to 0.7
Copper (Cu), % 0
95.3 to 97.8
Iron (Fe), % 69.3 to 77.3
0 to 0.25
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.45
0
Nickel (Ni), % 1.0 to 2.9
0 to 0.2
Nitrogen (N), % 0.16 to 0.28
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0.2 to 0.35
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0 to 0.1
Titanium (Ti), % 0
0 to 0.12
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.5