EN 1.4107 Stainless Steel vs. AISI 334 Stainless Steel

Both EN 1.4107 stainless steel and AISI 334 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4107 stainless steel and the bottom bar is AISI 334 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18 to 21
34
Fatigue Strength, MPa 260 to 350
150
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 620 to 700
540
Tensile Strength: Yield (Proof), MPa 400 to 570
190

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
490
Maximum Temperature: Mechanical, °C 740
1000
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1410
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 10
16

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.1
4.1
Embodied Energy, MJ/kg 30
59
Embodied Water, L/kg 100
170

Common Calculations

PREN (Pitting Resistance) 13
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
140
Resilience: Unit (Modulus of Resilience), kJ/m3 420 to 840
96
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22 to 25
19
Strength to Weight: Bending, points 21 to 22
19
Thermal Shock Resistance, points 22 to 25
12

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0 to 0.1
0 to 0.080
Chromium (Cr), % 11.5 to 12.5
18 to 20
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 83.8 to 87.2
55.7 to 62.7
Manganese (Mn), % 0.5 to 0.8
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0.8 to 1.5
19 to 21
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6
Vanadium (V), % 0 to 0.080
0