EN 1.4107 Stainless Steel vs. AWS E309LMo

Both EN 1.4107 stainless steel and AWS E309LMo are iron alloys. They have 73% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4107 stainless steel and the bottom bar is AWS E309LMo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18 to 21
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 620 to 700
580

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 27
15
Thermal Expansion, µm/m-K 10
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.1
4.2
Embodied Energy, MJ/kg 30
59
Embodied Water, L/kg 100
180

Common Calculations

PREN (Pitting Resistance) 13
32
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22 to 25
21
Strength to Weight: Bending, points 21 to 22
20
Thermal Diffusivity, mm2/s 7.2
3.9
Thermal Shock Resistance, points 22 to 25
15

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.040
Chromium (Cr), % 11.5 to 12.5
22 to 25
Copper (Cu), % 0 to 0.3
0 to 0.75
Iron (Fe), % 83.8 to 87.2
53.6 to 63.5
Manganese (Mn), % 0.5 to 0.8
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.5
2.0 to 3.0
Nickel (Ni), % 0.8 to 1.5
12 to 14
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030
Vanadium (V), % 0 to 0.080
0