MakeItFrom.com
Menu (ESC)

EN 1.4107 Stainless Steel vs. S34565 Stainless Steel

Both EN 1.4107 stainless steel and S34565 stainless steel are iron alloys. They have 62% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4107 stainless steel and the bottom bar is S34565 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 18 to 21
39
Fatigue Strength, MPa 260 to 350
400
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 620 to 700
900
Tensile Strength: Yield (Proof), MPa 400 to 570
470

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Maximum Temperature: Corrosion, °C 390
450
Maximum Temperature: Mechanical, °C 740
1100
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
12
Thermal Expansion, µm/m-K 10
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
28
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.1
5.3
Embodied Energy, MJ/kg 30
73
Embodied Water, L/kg 100
210

Common Calculations

PREN (Pitting Resistance) 13
47
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
300
Resilience: Unit (Modulus of Resilience), kJ/m3 420 to 840
540
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22 to 25
32
Strength to Weight: Bending, points 21 to 22
26
Thermal Diffusivity, mm2/s 7.2
3.2
Thermal Shock Resistance, points 22 to 25
22

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.030
Chromium (Cr), % 11.5 to 12.5
23 to 25
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 83.8 to 87.2
43.2 to 51.6
Manganese (Mn), % 0.5 to 0.8
5.0 to 7.0
Molybdenum (Mo), % 0 to 0.5
4.0 to 5.0
Nickel (Ni), % 0.8 to 1.5
16 to 18
Niobium (Nb), % 0
0 to 0.1
Nitrogen (N), % 0
0.4 to 0.6
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.010
Vanadium (V), % 0 to 0.080
0