EN 1.4110 Stainless Steel vs. EN 1.4606 Stainless Steel
Both EN 1.4110 stainless steel and EN 1.4606 stainless steel are iron alloys. They have 70% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.4110 stainless steel and the bottom bar is EN 1.4606 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 14 | |
| 23 to 39 |
| Fatigue Strength, MPa | 250 to 730 | |
| 240 to 420 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 75 |
| Shear Strength, MPa | 470 to 1030 | |
| 410 to 640 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 1720 | |
| 600 to 1020 |
| Tensile Strength: Yield (Proof), MPa | 430 to 1330 | |
| 280 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 770 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 910 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1430 |
| Melting Onset (Solidus), °C | 1400 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 30 | |
| 14 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.8 | |
| 1.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 2.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 26 |
| Density, g/cm3 | 7.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 6.0 |
| Embodied Energy, MJ/kg | 33 | |
| 87 |
| Embodied Water, L/kg | 110 | |
| 170 |
Common Calculations
| PREN (Pitting Resistance) | 16 | |
| 19 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 90 to 180 | |
| 190 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 480 to 4550 | |
| 200 to 1010 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 to 62 | |
| 21 to 36 |
| Strength to Weight: Bending, points | 24 to 41 | |
| 20 to 28 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 3.7 |
| Thermal Shock Resistance, points | 27 to 60 | |
| 21 to 35 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.35 |
| Boron (B), % | 0 | |
| 0.0010 to 0.010 |
| Carbon (C), % | 0.48 to 0.6 | |
| 0 to 0.080 |
| Chromium (Cr), % | 13 to 15 | |
| 13 to 16 |
| Iron (Fe), % | 81.4 to 86 | |
| 49.2 to 59 |
| Manganese (Mn), % | 0 to 1.0 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 0.5 to 0.8 | |
| 1.0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 24 to 27 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 1.9 to 2.3 |
| Vanadium (V), % | 0 to 0.15 | |
| 0.1 to 0.5 |