EN 1.4110 Stainless Steel vs. R58150 Titanium
EN 1.4110 stainless steel belongs to the iron alloys classification, while R58150 titanium belongs to the titanium alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.4110 stainless steel and the bottom bar is R58150 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 11 to 14 | |
| 13 |
| Fatigue Strength, MPa | 250 to 730 | |
| 330 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 76 | |
| 52 |
| Shear Strength, MPa | 470 to 1030 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 1720 | |
| 770 |
| Tensile Strength: Yield (Proof), MPa | 430 to 1330 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 320 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1760 |
| Melting Onset (Solidus), °C | 1400 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 500 |
| Thermal Expansion, µm/m-K | 11 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 48 |
| Density, g/cm3 | 7.7 | |
| 5.4 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 31 |
| Embodied Energy, MJ/kg | 33 | |
| 480 |
| Embodied Water, L/kg | 110 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 90 to 180 | |
| 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 480 to 4550 | |
| 1110 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 32 |
| Strength to Weight: Axial, points | 28 to 62 | |
| 40 |
| Strength to Weight: Bending, points | 24 to 41 | |
| 35 |
| Thermal Shock Resistance, points | 27 to 60 | |
| 48 |
Alloy Composition
| Carbon (C), % | 0.48 to 0.6 | |
| 0 to 0.1 |
| Chromium (Cr), % | 13 to 15 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 81.4 to 86 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 0.5 to 0.8 | |
| 14 to 16 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 83.5 to 86 |
| Vanadium (V), % | 0 to 0.15 | |
| 0 |