EN 1.4112 Stainless Steel vs. EN 1.5636 Steel

Both EN 1.4112 stainless steel and EN 1.5636 steel are iron alloys. They have 80% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4112 stainless steel and the bottom bar is EN 1.5636 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 20
27
Fatigue Strength, MPa 280
230
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 750
560
Tensile Strength: Yield (Proof), MPa 430
310

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 910
410
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 10
3.6
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.6
1.7
Embodied Energy, MJ/kg 37
23
Embodied Water, L/kg 130
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
130
Resilience: Unit (Modulus of Resilience), kJ/m3 480
260
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
20
Strength to Weight: Bending, points 24
19
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 26
16

Alloy Composition

Carbon (C), % 0.85 to 1.0
0.060 to 0.12
Chromium (Cr), % 17 to 19
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 76.6 to 81.2
94.6 to 97.4
Manganese (Mn), % 0 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 0.9 to 1.3
0 to 0.2
Nickel (Ni), % 0
2.0 to 3.0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.015
Vanadium (V), % 0.070 to 0.12
0 to 0.050