EN 1.4125 Stainless Steel vs. EN 1.0597 Cast Steel

Both EN 1.4125 stainless steel and EN 1.0597 cast steel are iron alloys. They have 80% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4125 stainless steel and the bottom bar is EN 1.0597 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 19
18
Fatigue Strength, MPa 300
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 800
670
Tensile Strength: Yield (Proof), MPa 470
400

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
400
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
1.7
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 32
18
Embodied Water, L/kg 120
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
100
Resilience: Unit (Modulus of Resilience), kJ/m3 570
430
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
24
Strength to Weight: Bending, points 25
22
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 29
21

Alloy Composition

Carbon (C), % 1.0 to 1.2
0
Chromium (Cr), % 16 to 18
0
Iron (Fe), % 78 to 82.7
99.935 to 100
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0.4 to 0.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0 to 0.030