EN 1.4125 Stainless Steel vs. EN 1.4107 Stainless Steel

Both EN 1.4125 stainless steel and EN 1.4107 stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4125 stainless steel and the bottom bar is EN 1.4107 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 19
18 to 21
Fatigue Strength, MPa 300
260 to 350
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 800
620 to 700
Tensile Strength: Yield (Proof), MPa 470
400 to 570

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Maximum Temperature: Corrosion, °C 390
390
Maximum Temperature: Mechanical, °C 870
740
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
27
Thermal Expansion, µm/m-K 10
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
7.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.3
2.1
Embodied Energy, MJ/kg 32
30
Embodied Water, L/kg 120
100

Common Calculations

PREN (Pitting Resistance) 19
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 570
420 to 840
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29
22 to 25
Strength to Weight: Bending, points 25
21 to 22
Thermal Diffusivity, mm2/s 4.1
7.2
Thermal Shock Resistance, points 29
22 to 25

Alloy Composition

Carbon (C), % 1.0 to 1.2
0 to 0.1
Chromium (Cr), % 16 to 18
11.5 to 12.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 78 to 82.7
83.8 to 87.2
Manganese (Mn), % 0 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 0.4 to 0.8
0 to 0.5
Nickel (Ni), % 0
0.8 to 1.5
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.020
Vanadium (V), % 0
0 to 0.080