EN 1.4150 Stainless Steel vs. EN 1.6526 Steel
Both EN 1.4150 stainless steel and EN 1.6526 steel are iron alloys. They have 83% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.4150 stainless steel and the bottom bar is EN 1.6526 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 | |
| 160 to 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 520 to 1460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 840 | |
| 410 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1380 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 470 |
| Thermal Conductivity, W/m-K | 23 | |
| 39 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.8 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.5 | |
| 2.6 |
| Density, g/cm3 | 7.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.5 |
| Embodied Energy, MJ/kg | 42 | |
| 20 |
| Embodied Water, L/kg | 120 | |
| 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 27 | |
| 18 to 52 |
| Strength to Weight: Bending, points | 24 | |
| 18 to 36 |
| Thermal Diffusivity, mm2/s | 6.2 | |
| 10 |
| Thermal Shock Resistance, points | 27 | |
| 15 to 43 |
Alloy Composition
| Carbon (C), % | 0.45 to 0.6 | |
| 0.17 to 0.23 |
| Chromium (Cr), % | 15 to 16.5 | |
| 0.35 to 0.7 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 79 to 82.8 | |
| 96.6 to 98.3 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0.65 to 1.0 |
| Molybdenum (Mo), % | 0.2 to 0.4 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 0 to 0.4 | |
| 0.4 to 0.7 |
| Nitrogen (N), % | 0.050 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 1.3 to 1.7 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.010 | |
| 0.020 to 0.040 |
| Vanadium (V), % | 0.2 to 0.4 | |
| 0 |