EN 1.4301 Stainless Steel vs. EN 1.4307 Stainless Steel
Both EN 1.4301 stainless steel and EN 1.4307 stainless steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.4301 stainless steel and the bottom bar is EN 1.4307 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 270 | |
| 180 to 270 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 14 to 46 | |
| 14 to 46 |
| Fatigue Strength, MPa | 200 to 330 | |
| 190 to 320 |
| Impact Strength: V-Notched Charpy, J | 91 to 94 | |
| 91 to 94 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 77 |
| Shear Strength, MPa | 430 to 550 | |
| 410 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 610 to 900 | |
| 590 to 900 |
| Tensile Strength: Yield (Proof), MPa | 220 to 570 | |
| 200 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 420 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 940 | |
| 940 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1430 |
| Melting Onset (Solidus), °C | 1380 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 15 |
| Thermal Expansion, µm/m-K | 16 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 15 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 3.0 |
| Embodied Energy, MJ/kg | 43 | |
| 43 |
| Embodied Water, L/kg | 140 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 19 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 220 | |
| 110 to 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 820 | |
| 100 to 810 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 32 | |
| 21 to 32 |
| Strength to Weight: Bending, points | 20 to 27 | |
| 20 to 27 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 4.0 |
| Thermal Shock Resistance, points | 14 to 20 | |
| 13 to 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.030 |
| Chromium (Cr), % | 17.5 to 19.5 | |
| 17.5 to 19.5 |
| Iron (Fe), % | 66.8 to 74.5 | |
| 66.8 to 74.5 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 8.0 to 10.5 | |
| 8.0 to 10.5 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |