EN 1.4305 Stainless Steel vs. EN 1.7272 Steel

Both EN 1.4305 stainless steel and EN 1.7272 steel are iron alloys. They have 72% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4305 stainless steel and the bottom bar is EN 1.7272 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 610 to 900
490 to 1650

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 930
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
45
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.5
Embodied Energy, MJ/kg 42
19
Embodied Water, L/kg 140
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22 to 32
17 to 59
Strength to Weight: Bending, points 20 to 27
18 to 40
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 14 to 20
14 to 48

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.1
0.28 to 0.33
Chromium (Cr), % 17 to 19
0.4 to 0.55
Copper (Cu), % 0 to 1.0
0 to 0.25
Iron (Fe), % 66.4 to 74.9
97.2 to 98.3
Manganese (Mn), % 0 to 2.0
0.9 to 1.2
Molybdenum (Mo), % 0
0.1 to 0.15
Nickel (Ni), % 8.0 to 10
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0.15 to 0.35
0 to 0.025

Comparable Variants