EN 1.4307 Stainless Steel vs. EN 1.0050 Steel

Both EN 1.4307 stainless steel and EN 1.0050 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is EN 1.0050 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 270
150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14 to 46
18
Fatigue Strength, MPa 190 to 320
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 410 to 550
330
Tensile Strength: Ultimate (UTS), MPa 590 to 900
530
Tensile Strength: Yield (Proof), MPa 200 to 570
280

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 940
400
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
6.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
7.8

Otherwise Unclassified Properties

Base Metal Price, % relative 15
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 43
18
Embodied Water, L/kg 140
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
81
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
210
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 32
19
Strength to Weight: Bending, points 20 to 27
18
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13 to 20
17

Alloy Composition

Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 17.5 to 19.5
0
Iron (Fe), % 66.8 to 74.5
99.876 to 100
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.0 to 10.5
0
Nitrogen (N), % 0 to 0.1
0 to 0.014
Phosphorus (P), % 0 to 0.045
0 to 0.055
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0 to 0.055