EN 1.4307 Stainless Steel vs. EN 1.1060 Steel

Both EN 1.4307 stainless steel and EN 1.1060 steel are iron alloys. They have 71% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is EN 1.1060 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 270
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 590 to 900
490 to 1720

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 940
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 15
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 43
18
Embodied Water, L/kg 140
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 32
17 to 61
Strength to Weight: Bending, points 20 to 27
18 to 41
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13 to 20
16 to 55

Alloy Composition

Carbon (C), % 0 to 0.030
0.32 to 0.39
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 66.8 to 74.5
98.2 to 99.16
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Nickel (Ni), % 8.0 to 10.5
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0.020 to 0.035

Comparable Variants