EN 1.4307 Stainless Steel vs. EN 1.4376 Stainless Steel

Both EN 1.4307 stainless steel and EN 1.4376 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is EN 1.4376 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 270
230
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 14 to 46
45
Fatigue Strength, MPa 190 to 320
420
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 410 to 550
530
Tensile Strength: Ultimate (UTS), MPa 590 to 900
750
Tensile Strength: Yield (Proof), MPa 200 to 570
450

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 420
420
Maximum Temperature: Mechanical, °C 940
930
Melting Completion (Liquidus), °C 1430
1410
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 15
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 43
37
Embodied Water, L/kg 140
140

Common Calculations

PREN (Pitting Resistance) 19
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
290
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
520
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 32
27
Strength to Weight: Bending, points 20 to 27
24
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 13 to 20
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 17.5 to 19.5
17 to 20.5
Iron (Fe), % 66.8 to 74.5
65.5 to 76
Manganese (Mn), % 0 to 2.0
5.0 to 8.0
Nickel (Ni), % 8.0 to 10.5
2.0 to 4.5
Nitrogen (N), % 0 to 0.1
0 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015