EN 1.4307 Stainless Steel vs. EN 1.4669 Stainless Steel

Both EN 1.4307 stainless steel and EN 1.4669 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is EN 1.4669 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 270
260
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 14 to 46
28
Fatigue Strength, MPa 190 to 320
330
Impact Strength: V-Notched Charpy, J 91 to 94
110
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
78
Shear Strength, MPa 410 to 550
500
Tensile Strength: Ultimate (UTS), MPa 590 to 900
780
Tensile Strength: Yield (Proof), MPa 200 to 570
450

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 420
440
Maximum Temperature: Mechanical, °C 940
1030
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 15
13
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 43
38
Embodied Water, L/kg 140
160

Common Calculations

PREN (Pitting Resistance) 19
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
190
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
510
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 32
28
Strength to Weight: Bending, points 20 to 27
24
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 13 to 20
21

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.045
Chromium (Cr), % 17.5 to 19.5
21.5 to 24
Copper (Cu), % 0
1.6 to 3.0
Iron (Fe), % 66.8 to 74.5
65.2 to 74.8
Manganese (Mn), % 0 to 2.0
1.0 to 3.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 8.0 to 10.5
1.0 to 3.0
Nitrogen (N), % 0 to 0.1
0.12 to 0.2
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030