EN 1.4307 Stainless Steel vs. EN 2.4964 Cobalt

EN 1.4307 stainless steel belongs to the iron alloys classification, while EN 2.4964 cobalt belongs to the cobalt alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is EN 2.4964 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Elongation at Break, % 14 to 46
40
Fatigue Strength, MPa 190 to 320
220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
86
Tensile Strength: Ultimate (UTS), MPa 590 to 900
960
Tensile Strength: Yield (Proof), MPa 200 to 570
390

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Melting Completion (Liquidus), °C 1430
1630
Melting Onset (Solidus), °C 1380
1550
Specific Heat Capacity, J/kg-K 480
400
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
1.8

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.6
Embodied Carbon, kg CO2/kg material 3.0
9.8
Embodied Energy, MJ/kg 43
140
Embodied Water, L/kg 140
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
310
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 21 to 32
28
Strength to Weight: Bending, points 20 to 27
23
Thermal Diffusivity, mm2/s 4.0
3.9
Thermal Shock Resistance, points 13 to 20
25

Alloy Composition

Carbon (C), % 0 to 0.030
0.050 to 0.15
Chromium (Cr), % 17.5 to 19.5
19 to 21
Cobalt (Co), % 0
46.4 to 58
Iron (Fe), % 66.8 to 74.5
0 to 3.0
Manganese (Mn), % 0 to 2.0
0 to 2.0
Nickel (Ni), % 8.0 to 10.5
9.0 to 11
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.015
Tungsten (W), % 0
14 to 16