EN 1.4307 Stainless Steel vs. CC480K Bronze

EN 1.4307 stainless steel belongs to the iron alloys classification, while CC480K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is CC480K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 270
88
Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 14 to 46
13
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
41
Tensile Strength: Ultimate (UTS), MPa 590 to 900
300
Tensile Strength: Yield (Proof), MPa 200 to 570
180

Thermal Properties

Latent Heat of Fusion, J/g 290
190
Maximum Temperature: Mechanical, °C 940
170
Melting Completion (Liquidus), °C 1430
1010
Melting Onset (Solidus), °C 1380
900
Specific Heat Capacity, J/kg-K 480
370
Thermal Conductivity, W/m-K 15
63
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
11
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
11

Otherwise Unclassified Properties

Base Metal Price, % relative 15
35
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 3.0
3.7
Embodied Energy, MJ/kg 43
59
Embodied Water, L/kg 140
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
35
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
140
Stiffness to Weight: Axial, points 14
6.9
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21 to 32
9.6
Strength to Weight: Bending, points 20 to 27
11
Thermal Diffusivity, mm2/s 4.0
20
Thermal Shock Resistance, points 13 to 20
11

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.2
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 0
86 to 90
Iron (Fe), % 66.8 to 74.5
0 to 0.2
Lead (Pb), % 0
0 to 1.0
Manganese (Mn), % 0 to 2.0
0 to 0.1
Nickel (Ni), % 8.0 to 10.5
0 to 2.0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.2
Silicon (Si), % 0 to 1.0
0 to 0.020
Sulfur (S), % 0 to 0.015
0 to 0.050
Tin (Sn), % 0
9.0 to 11
Zinc (Zn), % 0
0 to 0.5