EN 1.4307 Stainless Steel vs. C63000 Bronze

EN 1.4307 stainless steel belongs to the iron alloys classification, while C63000 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is C63000 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 14 to 46
7.9 to 15
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
44
Shear Strength, MPa 410 to 550
400 to 470
Tensile Strength: Ultimate (UTS), MPa 590 to 900
660 to 790
Tensile Strength: Yield (Proof), MPa 200 to 570
330 to 390

Thermal Properties

Latent Heat of Fusion, J/g 290
230
Maximum Temperature: Mechanical, °C 940
230
Melting Completion (Liquidus), °C 1430
1050
Melting Onset (Solidus), °C 1380
1040
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
7.6

Otherwise Unclassified Properties

Base Metal Price, % relative 15
29
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 3.0
3.5
Embodied Energy, MJ/kg 43
57
Embodied Water, L/kg 140
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
47 to 82
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
470 to 640
Stiffness to Weight: Axial, points 14
7.9
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 21 to 32
22 to 26
Strength to Weight: Bending, points 20 to 27
20 to 23
Thermal Diffusivity, mm2/s 4.0
11
Thermal Shock Resistance, points 13 to 20
23 to 27

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
9.0 to 11
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 0
76.8 to 85
Iron (Fe), % 66.8 to 74.5
2.0 to 4.0
Manganese (Mn), % 0 to 2.0
0 to 1.5
Nickel (Ni), % 8.0 to 10.5
4.0 to 5.5
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0 to 0.25
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.3
Residuals, % 0
0 to 0.5