EN 1.4307 Stainless Steel vs. C69300 Brass

EN 1.4307 stainless steel belongs to the iron alloys classification, while C69300 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is C69300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 14 to 46
8.5 to 15
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 77
41
Shear Strength, MPa 410 to 550
330 to 370
Tensile Strength: Ultimate (UTS), MPa 590 to 900
550 to 630
Tensile Strength: Yield (Proof), MPa 200 to 570
300 to 390

Thermal Properties

Latent Heat of Fusion, J/g 290
240
Maximum Temperature: Mechanical, °C 940
160
Melting Completion (Liquidus), °C 1430
880
Melting Onset (Solidus), °C 1380
860
Specific Heat Capacity, J/kg-K 480
400
Thermal Conductivity, W/m-K 15
38
Thermal Expansion, µm/m-K 16
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 15
26
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 3.0
2.7
Embodied Energy, MJ/kg 43
45
Embodied Water, L/kg 140
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
47 to 70
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
400 to 700
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 21 to 32
19 to 21
Strength to Weight: Bending, points 20 to 27
18 to 20
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 13 to 20
19 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 0
73 to 77
Iron (Fe), % 66.8 to 74.5
0 to 0.1
Lead (Pb), % 0
0 to 0.090
Manganese (Mn), % 0 to 2.0
0 to 0.1
Nickel (Ni), % 8.0 to 10.5
0 to 0.1
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0.040 to 0.15
Silicon (Si), % 0 to 1.0
2.7 to 3.4
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 0
18.4 to 24.3
Residuals, % 0
0 to 0.5