EN 1.4307 Stainless Steel vs. S39274 Stainless Steel

Both EN 1.4307 stainless steel and S39274 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is S39274 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 270
270
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 14 to 46
17
Fatigue Strength, MPa 190 to 320
380
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
81
Shear Strength, MPa 410 to 550
560
Tensile Strength: Ultimate (UTS), MPa 590 to 900
900
Tensile Strength: Yield (Proof), MPa 200 to 570
620

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 420
450
Maximum Temperature: Mechanical, °C 940
1100
Melting Completion (Liquidus), °C 1430
1480
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 15
24
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.0
4.3
Embodied Energy, MJ/kg 43
60
Embodied Water, L/kg 140
180

Common Calculations

PREN (Pitting Resistance) 19
43
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
140
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
940
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 32
32
Strength to Weight: Bending, points 20 to 27
26
Thermal Diffusivity, mm2/s 4.0
4.2
Thermal Shock Resistance, points 13 to 20
25

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 17.5 to 19.5
24 to 26
Copper (Cu), % 0
0.2 to 0.8
Iron (Fe), % 66.8 to 74.5
57 to 65.6
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 8.0 to 10.5
6.0 to 8.0
Nitrogen (N), % 0 to 0.1
0.24 to 0.32
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.020
Tungsten (W), % 0
1.5 to 2.5