EN 1.4307 Stainless Steel vs. S42010 Stainless Steel

Both EN 1.4307 stainless steel and S42010 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is S42010 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 14 to 46
18
Fatigue Strength, MPa 190 to 320
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Shear Strength, MPa 410 to 550
370
Tensile Strength: Ultimate (UTS), MPa 590 to 900
590
Tensile Strength: Yield (Proof), MPa 200 to 570
350

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 420
390
Maximum Temperature: Mechanical, °C 940
800
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
29
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 15
8.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.2
Embodied Energy, MJ/kg 43
30
Embodied Water, L/kg 140
110

Common Calculations

PREN (Pitting Resistance) 19
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
95
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 32
21
Strength to Weight: Bending, points 20 to 27
20
Thermal Diffusivity, mm2/s 4.0
7.9
Thermal Shock Resistance, points 13 to 20
21

Alloy Composition

Carbon (C), % 0 to 0.030
0.15 to 0.3
Chromium (Cr), % 17.5 to 19.5
13.5 to 15
Iron (Fe), % 66.8 to 74.5
80.9 to 85.6
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0.4 to 0.85
Nickel (Ni), % 8.0 to 10.5
0.35 to 0.85
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030