MakeItFrom.com
Menu (ESC)

EN 1.4307 Stainless Steel vs. ZA-8

EN 1.4307 stainless steel belongs to the iron alloys classification, while ZA-8 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4307 stainless steel and the bottom bar is ZA-8.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 270
87 to 100
Elastic (Young's, Tensile) Modulus, GPa 200
85 to 86
Elongation at Break, % 14 to 46
1.3 to 8.0
Fatigue Strength, MPa 190 to 320
51 to 100
Poisson's Ratio 0.28
0.26
Shear Modulus, GPa 77
34
Shear Strength, MPa 410 to 550
240 to 280
Tensile Strength: Ultimate (UTS), MPa 590 to 900
210 to 370
Tensile Strength: Yield (Proof), MPa 200 to 570
210 to 290

Thermal Properties

Latent Heat of Fusion, J/g 290
110
Maximum Temperature: Mechanical, °C 940
100
Melting Completion (Liquidus), °C 1430
400
Melting Onset (Solidus), °C 1380
380
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 15
120
Thermal Expansion, µm/m-K 16
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
28
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
40

Otherwise Unclassified Properties

Base Metal Price, % relative 15
11
Density, g/cm3 7.8
6.3
Embodied Carbon, kg CO2/kg material 3.0
3.3
Embodied Energy, MJ/kg 43
62
Embodied Water, L/kg 140
420

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 210
2.8 to 28
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 810
260 to 490
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 21 to 32
9.3 to 17
Strength to Weight: Bending, points 20 to 27
12 to 18
Thermal Diffusivity, mm2/s 4.0
42
Thermal Shock Resistance, points 13 to 20
7.6 to 13

Alloy Composition

Aluminum (Al), % 0
8.0 to 8.8
Cadmium (Cd), % 0
0 to 0.0060
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 0
0.8 to 1.3
Iron (Fe), % 66.8 to 74.5
0 to 0.075
Lead (Pb), % 0
0 to 0.0060
Magnesium (Mg), % 0
0.015 to 0.030
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.0 to 10.5
0 to 0.020
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0 to 0.045
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0
89.7 to 91.2

Comparable Variants