MakeItFrom.com
Menu (ESC)

EN 1.4308 Stainless Steel vs. 6151 Aluminum

EN 1.4308 stainless steel belongs to the iron alloys classification, while 6151 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is 6151 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
69
Elongation at Break, % 34
1.1 to 5.7
Fatigue Strength, MPa 160
80 to 100
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 77
26
Tensile Strength: Ultimate (UTS), MPa 510
330 to 340
Tensile Strength: Yield (Proof), MPa 200
270 to 280

Thermal Properties

Latent Heat of Fusion, J/g 290
410
Maximum Temperature: Mechanical, °C 960
170
Melting Completion (Liquidus), °C 1420
650
Melting Onset (Solidus), °C 1380
590
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 15
170
Thermal Expansion, µm/m-K 17
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
45
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
150

Otherwise Unclassified Properties

Base Metal Price, % relative 15
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 3.0
8.2
Embodied Energy, MJ/kg 43
150
Embodied Water, L/kg 150
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
3.5 to 18
Resilience: Unit (Modulus of Resilience), kJ/m3 100
520 to 580
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
50
Strength to Weight: Axial, points 18
34
Strength to Weight: Bending, points 18
39
Thermal Diffusivity, mm2/s 4.1
70
Thermal Shock Resistance, points 11
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
95.6 to 98.8
Carbon (C), % 0 to 0.070
0
Chromium (Cr), % 18 to 20
0.15 to 0.35
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 65.9 to 74
0 to 1.0
Magnesium (Mg), % 0
0.45 to 0.8
Manganese (Mn), % 0 to 1.5
0 to 0.2
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0.6 to 1.2
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.15
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0
0 to 0.15