EN 1.4308 Stainless Steel vs. AISI 440A Stainless Steel

Both EN 1.4308 stainless steel and AISI 440A stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is AISI 440A stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
5.0 to 20
Fatigue Strength, MPa 160
270 to 790
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 510
730 to 1790
Tensile Strength: Yield (Proof), MPa 200
420 to 1650

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 420
400
Maximum Temperature: Mechanical, °C 960
760
Melting Completion (Liquidus), °C 1420
1480
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
23
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 15
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.2
Embodied Energy, MJ/kg 43
31
Embodied Water, L/kg 150
120

Common Calculations

PREN (Pitting Resistance) 19
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
87 to 120
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
26 to 65
Strength to Weight: Bending, points 18
23 to 43
Thermal Diffusivity, mm2/s 4.1
6.2
Thermal Shock Resistance, points 11
26 to 65

Alloy Composition

Carbon (C), % 0 to 0.070
0.6 to 0.75
Chromium (Cr), % 18 to 20
16 to 18
Iron (Fe), % 65.9 to 74
78.4 to 83.4
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015