EN 1.4308 Stainless Steel vs. AWS E308L

Both EN 1.4308 stainless steel and AWS E308L are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is AWS E308L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
40
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 510
580

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 17
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 15
16
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
3.2
Embodied Energy, MJ/kg 43
46
Embodied Water, L/kg 150
150

Common Calculations

PREN (Pitting Resistance) 19
21
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 4.1
4.1
Thermal Shock Resistance, points 11
15

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.040
Chromium (Cr), % 18 to 20
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 65.9 to 74
62.9 to 72.5
Manganese (Mn), % 0 to 1.5
0.5 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 8.0 to 11
9.0 to 11
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030