EN 1.4308 Stainless Steel vs. EN 1.4303 Stainless Steel

Both EN 1.4308 stainless steel and EN 1.4303 stainless steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is EN 1.4303 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
13 to 49
Fatigue Strength, MPa 160
220 to 320
Impact Strength: V-Notched Charpy, J 67
91 to 98
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 510
590 to 900
Tensile Strength: Yield (Proof), MPa 200
230 to 560

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 960
940
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 15
17
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
3.2
Embodied Energy, MJ/kg 43
46
Embodied Water, L/kg 150
150

Common Calculations

PREN (Pitting Resistance) 19
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 100
140 to 800
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
21 to 32
Strength to Weight: Bending, points 18
20 to 26
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 11
13 to 20

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.060
Chromium (Cr), % 18 to 20
17 to 19
Iron (Fe), % 65.9 to 74
64.8 to 72
Manganese (Mn), % 0 to 1.5
0 to 2.0
Nickel (Ni), % 8.0 to 11
11 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015