EN 1.4308 Stainless Steel vs. EN 1.8503 Steel

Both EN 1.4308 stainless steel and EN 1.8503 steel are iron alloys. They have 72% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is EN 1.8503 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
300
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
16
Fatigue Strength, MPa 160
600
Impact Strength: V-Notched Charpy, J 67
39
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 510
1000
Tensile Strength: Yield (Proof), MPa 200
910

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 960
440
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
41
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 15
3.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
2.3
Embodied Energy, MJ/kg 43
33
Embodied Water, L/kg 150
57

Common Calculations

PREN (Pitting Resistance) 19
3.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
150
Resilience: Unit (Modulus of Resilience), kJ/m3 100
2200
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
35
Strength to Weight: Bending, points 18
28
Thermal Diffusivity, mm2/s 4.1
11
Thermal Shock Resistance, points 11
29

Alloy Composition

Aluminum (Al), % 0
0 to 0.3
Carbon (C), % 0 to 0.070
0.16 to 0.24
Chromium (Cr), % 18 to 20
1.2 to 1.5
Iron (Fe), % 65.9 to 74
95.8 to 97.5
Manganese (Mn), % 0 to 1.5
0.4 to 0.8
Molybdenum (Mo), % 0
0.65 to 0.8
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035
Vanadium (V), % 0
0.25 to 0.35