MakeItFrom.com
Menu (ESC)

EN 1.4308 Stainless Steel vs. SAE-AISI 1008 Steel

Both EN 1.4308 stainless steel and SAE-AISI 1008 steel are iron alloys. They have 70% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is SAE-AISI 1008 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
93 to 100
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
22 to 33
Fatigue Strength, MPa 160
150 to 220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 510
330 to 370
Tensile Strength: Yield (Proof), MPa 200
190 to 310

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 960
400
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
62
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 15
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 43
18
Embodied Water, L/kg 150
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
78 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 100
92 to 260
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
12 to 13
Strength to Weight: Bending, points 18
13 to 15
Thermal Diffusivity, mm2/s 4.1
17
Thermal Shock Resistance, points 11
10 to 12

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.1
Chromium (Cr), % 18 to 20
0
Iron (Fe), % 65.9 to 74
99.31 to 99.7
Manganese (Mn), % 0 to 1.5
0.3 to 0.5
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0
Sulfur (S), % 0 to 0.030
0 to 0.050