EN 1.4308 Stainless Steel vs. N06045 Nickel

EN 1.4308 stainless steel belongs to the iron alloys classification, while N06045 nickel belongs to the nickel alloys. They have 53% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is N06045 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
37
Fatigue Strength, MPa 160
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 510
690
Tensile Strength: Yield (Proof), MPa 200
270

Thermal Properties

Latent Heat of Fusion, J/g 290
350
Maximum Temperature: Mechanical, °C 960
1010
Melting Completion (Liquidus), °C 1420
1350
Melting Onset (Solidus), °C 1380
1300
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 17
13

Otherwise Unclassified Properties

Base Metal Price, % relative 15
42
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.0
6.9
Embodied Energy, MJ/kg 43
98
Embodied Water, L/kg 150
250

Common Calculations

PREN (Pitting Resistance) 19
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
200
Resilience: Unit (Modulus of Resilience), kJ/m3 100
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
24
Strength to Weight: Bending, points 18
22
Thermal Shock Resistance, points 11
18

Alloy Composition

Carbon (C), % 0 to 0.070
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 18 to 20
26 to 29
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 65.9 to 74
21 to 25
Manganese (Mn), % 0 to 1.5
0 to 1.0
Nickel (Ni), % 8.0 to 11
45 to 50.4
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.5
2.5 to 3.0
Sulfur (S), % 0 to 0.030
0 to 0.010