EN 1.4308 Stainless Steel vs. N06219 Nickel

EN 1.4308 stainless steel belongs to the iron alloys classification, while N06219 nickel belongs to the nickel alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is N06219 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
48
Fatigue Strength, MPa 160
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 510
730
Tensile Strength: Yield (Proof), MPa 200
300

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Maximum Temperature: Mechanical, °C 960
980
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 15
10
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 15
60
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 3.0
11
Embodied Energy, MJ/kg 43
140
Embodied Water, L/kg 150
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
280
Resilience: Unit (Modulus of Resilience), kJ/m3 100
230
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 18
24
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 4.1
2.7
Thermal Shock Resistance, points 11
21

Alloy Composition

Aluminum (Al), % 0
0 to 0.5
Carbon (C), % 0 to 0.070
0 to 0.050
Chromium (Cr), % 18 to 20
18 to 22
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 65.9 to 74
2.0 to 4.0
Manganese (Mn), % 0 to 1.5
0 to 0.5
Molybdenum (Mo), % 0
7.0 to 9.0
Nickel (Ni), % 8.0 to 11
60.8 to 72.3
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.5
0.7 to 1.1
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.5