EN 1.4308 Stainless Steel vs. N07750 Nickel

EN 1.4308 stainless steel belongs to the iron alloys classification, while N07750 nickel belongs to the nickel alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4308 stainless steel and the bottom bar is N07750 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
25
Fatigue Strength, MPa 160
520
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 510
1200
Tensile Strength: Yield (Proof), MPa 200
820

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Maximum Temperature: Mechanical, °C 960
960
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 15
60
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 3.0
10
Embodied Energy, MJ/kg 43
150
Embodied Water, L/kg 150
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
270
Resilience: Unit (Modulus of Resilience), kJ/m3 100
1770
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 18
40
Strength to Weight: Bending, points 18
30
Thermal Diffusivity, mm2/s 4.1
3.3
Thermal Shock Resistance, points 11
36

Alloy Composition

Aluminum (Al), % 0
0.4 to 1.0
Carbon (C), % 0 to 0.070
0 to 0.080
Chromium (Cr), % 18 to 20
14 to 17
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 65.9 to 74
5.0 to 9.0
Manganese (Mn), % 0 to 1.5
0 to 1.0
Nickel (Ni), % 8.0 to 11
70 to 77.7
Niobium (Nb), % 0
0.7 to 1.2
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
2.3 to 2.8