EN 1.4310 Stainless Steel vs. EN 1.1165 Cast Steel
Both EN 1.4310 stainless steel and EN 1.1165 cast steel are iron alloys. They have 74% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4310 stainless steel and the bottom bar is EN 1.1165 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 14 to 45 | |
| 11 to 20 |
| Fatigue Strength, MPa | 240 to 330 | |
| 200 to 380 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 900 | |
| 600 to 780 |
| Tensile Strength: Yield (Proof), MPa | 260 to 570 | |
| 290 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 400 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1380 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 51 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 8.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 42 | |
| 19 |
| Embodied Water, L/kg | 140 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 260 | |
| 81 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 830 | |
| 230 to 1010 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 32 | |
| 21 to 28 |
| Strength to Weight: Bending, points | 23 to 27 | |
| 20 to 24 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 14 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 19 to 25 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.15 | |
| 0.25 to 0.32 |
| Chromium (Cr), % | 16 to 19 | |
| 0 |
| Iron (Fe), % | 66.4 to 78 | |
| 97.2 to 98.6 |
| Manganese (Mn), % | 0 to 2.0 | |
| 1.2 to 1.8 |
| Molybdenum (Mo), % | 0 to 0.8 | |
| 0 |
| Nickel (Ni), % | 6.0 to 9.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 2.0 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |