EN 1.4317 Stainless Steel vs. C69430 Brass

EN 1.4317 stainless steel belongs to the iron alloys classification, while C69430 brass belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4317 stainless steel and the bottom bar is C69430 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 17
17
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
42
Tensile Strength: Ultimate (UTS), MPa 860
570
Tensile Strength: Yield (Proof), MPa 630
280

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Maximum Temperature: Mechanical, °C 770
170
Melting Completion (Liquidus), °C 1440
920
Melting Onset (Solidus), °C 1400
820
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 26
26
Thermal Expansion, µm/m-K 11
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
6.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
6.7

Otherwise Unclassified Properties

Base Metal Price, % relative 10
27
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 2.4
2.7
Embodied Energy, MJ/kg 33
44
Embodied Water, L/kg 110
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
80
Resilience: Unit (Modulus of Resilience), kJ/m3 1010
340
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 31
19
Strength to Weight: Bending, points 26
18
Thermal Diffusivity, mm2/s 7.0
7.7
Thermal Shock Resistance, points 30
20

Alloy Composition

Arsenic (As), % 0
0.030 to 0.060
Carbon (C), % 0 to 0.060
0
Chromium (Cr), % 12 to 13.5
0
Copper (Cu), % 0
80 to 83
Iron (Fe), % 78.7 to 84.5
0 to 0.2
Lead (Pb), % 0
0 to 0.3
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0 to 0.7
0
Nickel (Ni), % 3.5 to 5.0
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
3.5 to 4.5
Sulfur (S), % 0 to 0.025
0
Zinc (Zn), % 0
11.4 to 16.5
Residuals, % 0
0 to 0.5