EN 1.4319 Stainless Steel vs. ACI-ASTM CE30 Steel

Both EN 1.4319 stainless steel and ACI-ASTM CE30 steel are iron alloys. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4319 stainless steel and the bottom bar is ACI-ASTM CE30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 51
11
Fatigue Strength, MPa 240
170
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 640
630
Tensile Strength: Yield (Proof), MPa 250
310

Thermal Properties

Latent Heat of Fusion, J/g 280
310
Maximum Temperature: Corrosion, °C 410
460
Maximum Temperature: Mechanical, °C 890
1100
Melting Completion (Liquidus), °C 1430
1410
Melting Onset (Solidus), °C 1390
1360
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 13
19
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.7
3.4
Embodied Energy, MJ/kg 39
49
Embodied Water, L/kg 130
180

Common Calculations

PREN (Pitting Resistance) 18
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
59
Resilience: Unit (Modulus of Resilience), kJ/m3 160
240
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
23
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 4.0
3.6
Thermal Shock Resistance, points 14
13

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.3
Chromium (Cr), % 16 to 18
26 to 30
Iron (Fe), % 70.8 to 78
55.1 to 66
Manganese (Mn), % 0 to 2.0
0 to 1.5
Nickel (Ni), % 6.0 to 8.0
8.0 to 11
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.040