EN 1.4319 Stainless Steel vs. EN 1.4125 Stainless Steel

Both EN 1.4319 stainless steel and EN 1.4125 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4319 stainless steel and the bottom bar is EN 1.4125 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
250
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 51
19
Fatigue Strength, MPa 240
300
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 460
500
Tensile Strength: Ultimate (UTS), MPa 640
800
Tensile Strength: Yield (Proof), MPa 250
470

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Maximum Temperature: Corrosion, °C 410
390
Maximum Temperature: Mechanical, °C 890
870
Melting Completion (Liquidus), °C 1430
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.7
2.3
Embodied Energy, MJ/kg 39
32
Embodied Water, L/kg 130
120

Common Calculations

PREN (Pitting Resistance) 18
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
130
Resilience: Unit (Modulus of Resilience), kJ/m3 160
570
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
29
Strength to Weight: Bending, points 21
25
Thermal Diffusivity, mm2/s 4.0
4.1
Thermal Shock Resistance, points 14
29

Alloy Composition

Carbon (C), % 0 to 0.070
1.0 to 1.2
Chromium (Cr), % 16 to 18
16 to 18
Iron (Fe), % 70.8 to 78
78 to 82.7
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
0.4 to 0.8
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015