EN 1.4319 Stainless Steel vs. EN 1.4584 Stainless Steel

Both EN 1.4319 stainless steel and EN 1.4584 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 72% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4319 stainless steel and the bottom bar is EN 1.4584 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 51
34
Fatigue Strength, MPa 240
170
Impact Strength: V-Notched Charpy, J 91
67
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 640
500
Tensile Strength: Yield (Proof), MPa 250
210

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 890
1100
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
31
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 2.7
5.7
Embodied Energy, MJ/kg 39
78
Embodied Water, L/kg 130
200

Common Calculations

PREN (Pitting Resistance) 18
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
140
Resilience: Unit (Modulus of Resilience), kJ/m3 160
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 4.0
4.5
Thermal Shock Resistance, points 14
12

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.025
Chromium (Cr), % 16 to 18
19 to 21
Copper (Cu), % 0
1.0 to 3.0
Iron (Fe), % 70.8 to 78
41.7 to 52
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 6.0 to 8.0
24 to 26
Nitrogen (N), % 0 to 0.1
0 to 0.2
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.020