EN 1.4319 Stainless Steel vs. EN 1.5410 Steel

Both EN 1.4319 stainless steel and EN 1.5410 steel are iron alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4319 stainless steel and the bottom bar is EN 1.5410 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170 to 190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 51
20 to 25
Fatigue Strength, MPa 240
290 to 330
Impact Strength: V-Notched Charpy, J 91
67 to 68
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 640
560 to 620
Tensile Strength: Yield (Proof), MPa 250
400 to 480

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 890
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.7
Embodied Energy, MJ/kg 39
22
Embodied Water, L/kg 130
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 160
430 to 610
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
20 to 22
Strength to Weight: Bending, points 21
19 to 21
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 14
16 to 18

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.12
Chromium (Cr), % 16 to 18
0
Iron (Fe), % 70.8 to 78
96.9 to 98.6
Manganese (Mn), % 0 to 2.0
1.2 to 1.8
Molybdenum (Mo), % 0
0.2 to 0.4
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0
0.050 to 0.1