EN 1.4319 Stainless Steel vs. EN 1.5663 Steel

Both EN 1.4319 stainless steel and EN 1.5663 steel are iron alloys. They have 82% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4319 stainless steel and the bottom bar is EN 1.5663 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 51
20
Fatigue Strength, MPa 240
450
Impact Strength: V-Notched Charpy, J 91
120
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 460
470
Tensile Strength: Ultimate (UTS), MPa 640
750
Tensile Strength: Yield (Proof), MPa 250
660

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 890
430
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
8.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
9.8

Otherwise Unclassified Properties

Base Metal Price, % relative 13
7.5
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 2.7
2.3
Embodied Energy, MJ/kg 39
31
Embodied Water, L/kg 130
63

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
150
Resilience: Unit (Modulus of Resilience), kJ/m3 160
1150
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
26
Strength to Weight: Bending, points 21
23
Thermal Shock Resistance, points 14
22

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.1
Chromium (Cr), % 16 to 18
0
Iron (Fe), % 70.8 to 78
88.6 to 91.2
Manganese (Mn), % 0 to 2.0
0.3 to 0.8
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 6.0 to 8.0
8.5 to 10
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.0050
Vanadium (V), % 0
0 to 0.010