EN 1.4371 Stainless Steel vs. N07776 Nickel

EN 1.4371 stainless steel belongs to the iron alloys classification, while N07776 nickel belongs to the nickel alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4371 stainless steel and the bottom bar is N07776 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45 to 51
39
Fatigue Strength, MPa 290 to 340
220
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 77
79
Shear Strength, MPa 520 to 540
470
Tensile Strength: Ultimate (UTS), MPa 740 to 750
700
Tensile Strength: Yield (Proof), MPa 320 to 340
270

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Mechanical, °C 880
970
Melting Completion (Liquidus), °C 1410
1550
Melting Onset (Solidus), °C 1370
1500
Specific Heat Capacity, J/kg-K 480
430
Thermal Expansion, µm/m-K 17
12

Otherwise Unclassified Properties

Base Metal Price, % relative 12
85
Density, g/cm3 7.7
8.6
Embodied Carbon, kg CO2/kg material 2.6
15
Embodied Energy, MJ/kg 38
210
Embodied Water, L/kg 140
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270 to 310
220
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 300
180
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 27
22
Strength to Weight: Bending, points 24
20
Thermal Shock Resistance, points 16
20

Alloy Composition

Aluminum (Al), % 0
0 to 2.0
Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 16 to 17.5
12 to 22
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 66.7 to 74.4
0 to 24.5
Manganese (Mn), % 6.0 to 8.0
0 to 1.0
Molybdenum (Mo), % 0
9.0 to 15
Nickel (Ni), % 3.5 to 5.5
50 to 60
Niobium (Nb), % 0
4.0 to 6.0
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 0
0 to 1.0
Tungsten (W), % 0
0.5 to 2.5